A comprehensive study on removal of cadmium from aqueous solution by using mesoporous SBA-15 functionalized by 1,5-diphenyl carbazide: experimental design, kinetic, thermodynamic, and isotherm aspects
Comptes Rendus. Chimie, Volume 24 (2021) no. 1, pp. 43-59.

Résumé

In this study, a new adsorbent, which was synthesized by using SBA-15Santa Barbara Amorphous. modified with 1,5-diphenyl carbazide, was employed to extract cadmium (Cd) from aquatic systems. First, the sorbent was identified via various characterization techniques, and then the response surface methodology approach was applied for modeling and optimizing the adsorption performance of the sorbent. Under optimum conditions (pH=5.75, an adsorbent dose of 4.55 mg, and a Cd concentration of 25.39 mg/L), an adsorption capacity of 160 mg/g was obtained. In addition, the sorption process was fast; it attained equilibrium in 25.39 min. Furthermore, the sorbent regenerated by nitric acid was reused without any significant loss of adsorption capacity. Finally, the experimental data were studied by different isotherm models and well described by the Langmuir model.

Supplementary Materials:
Supplementary material for this article is supplied as a separate file:

Métadonnées
Reçu le :
Révisé le :
Accepté le :
Publié le :
DOI : 10.5802/crchim.55
Mots clés : Cadmium removal, Functionalized SBA-15, 1, 5-diphenyl carbazide, Adsorption, Response surface methodology
Maryam Danesh-Khorasgani 1 ; Hossein Faghihian 2 ; Mohammad Hadi Givianrad 1 ; Parviz Aberoomand-Azar 1 ; Mohammad Saber-Tehrani 1

1 Department of Chemistry, Science and Research Branch, Islamic Azad University, P.O. Box 21-14515/755, Tehran, Iran
2 Department of Chemistry, Shahreza Branch, Islamic Azad University, P.O. Box 311-86145, Shahreza, Iran
Licence : CC-BY 4.0
Droits d'auteur : Les auteurs conservent leurs droits
@article{CRCHIM_2021__24_1_43_0,
     author = {Maryam Danesh-Khorasgani and Hossein Faghihian and Mohammad Hadi Givianrad and Parviz Aberoomand-Azar and Mohammad Saber-Tehrani},
     title = {A comprehensive study on removal of cadmium from aqueous solution by using mesoporous {SBA-15} functionalized by 1,5-diphenyl carbazide: experimental design, kinetic, thermodynamic, and isotherm aspects},
     journal = {Comptes Rendus. Chimie},
     pages = {43--59},
     publisher = {Acad\'emie des sciences, Paris},
     volume = {24},
     number = {1},
     year = {2021},
     doi = {10.5802/crchim.55},
     language = {en},
}
TY  - JOUR
AU  - Maryam Danesh-Khorasgani
AU  - Hossein Faghihian
AU  - Mohammad Hadi Givianrad
AU  - Parviz Aberoomand-Azar
AU  - Mohammad Saber-Tehrani
TI  - A comprehensive study on removal of cadmium from aqueous solution by using mesoporous SBA-15 functionalized by 1,5-diphenyl carbazide: experimental design, kinetic, thermodynamic, and isotherm aspects
JO  - Comptes Rendus. Chimie
PY  - 2021
SP  - 43
EP  - 59
VL  - 24
IS  - 1
PB  - Académie des sciences, Paris
DO  - 10.5802/crchim.55
LA  - en
ID  - CRCHIM_2021__24_1_43_0
ER  - 
%0 Journal Article
%A Maryam Danesh-Khorasgani
%A Hossein Faghihian
%A Mohammad Hadi Givianrad
%A Parviz Aberoomand-Azar
%A Mohammad Saber-Tehrani
%T A comprehensive study on removal of cadmium from aqueous solution by using mesoporous SBA-15 functionalized by 1,5-diphenyl carbazide: experimental design, kinetic, thermodynamic, and isotherm aspects
%J Comptes Rendus. Chimie
%D 2021
%P 43-59
%V 24
%N 1
%I Académie des sciences, Paris
%R 10.5802/crchim.55
%G en
%F CRCHIM_2021__24_1_43_0
Maryam Danesh-Khorasgani; Hossein Faghihian; Mohammad Hadi Givianrad; Parviz Aberoomand-Azar; Mohammad Saber-Tehrani. A comprehensive study on removal of cadmium from aqueous solution by using mesoporous SBA-15 functionalized by 1,5-diphenyl carbazide: experimental design, kinetic, thermodynamic, and isotherm aspects. Comptes Rendus. Chimie, Volume 24 (2021) no. 1, pp. 43-59. doi : 10.5802/crchim.55. https://comptes-rendus.academie-sciences.fr/chimie/articles/10.5802/crchim.55/

Version originale du texte intégral (Proposez une traduction )


1. Introduction

The growth in world population and industrial activities has resulted in the discharge of various dyes [1, 2], pharmaceuticals and antibiotics [3, 4, 5], numerous organic compounds, especially aromatic compounds [6, 7, 8], and heavy metals [9, 10, 11] into the environment, particularly into aquatic habitats. Among them, heavy metal cations have severe negative impacts on the environment and humans because they tend to accumulate in human tissues without undergoing biodegradation [12, 13, 14, 15, 16]. Ecosystems are polluted by heavy elements through natural or artificial routes. Natural contamination occurs by rainfall and through the release of bedrock and soil into the environment. Artificial routes of contamination include urban and industrial wastes, mining, and agricultural activities [17, 18]. Different industries act as the major source of cadmium (Cd) released into the environment in the form of ceramics, paints, plastics, and pigments and through processes such as electroplating, metallurgy, and battery manufacturing [19]. The risk of human exposure to Cd has risen through the increase in contamination of the food chain [20]. The World Health Organization has set a permissible limit of 0.003 mg/L for Cd in drinking water. Regarding the deleterious effects of Cd on ecosystems, the removal of cations from aquatic systems is inevitable for environmental remediation. In many polluted systems, various contaminants with different permissible limits may coexist. Therefore, the development of a selective separation technique for each pollutant is necessary for achieving their efficient removal from aquatic environments. [19].

Various methods such as ion exchange [21], chemical precipitation [22], flotation [23], ultrafiltration [24], nanofiltration [25], reverse osmosis [26], and electrocoagulation have been used to remove heavy element cations [27]. The adsorption process, among others, proven to be the most practical technique for wastewater treatment [12]. However, preparing adequate sorbents with desirable selectivity and sufficient capacity for the effective removal of target cations remains a key topic of research [19].

Mesoporous materials are widely employed for cation removal due to their large surface area, high porosity, and environmental-friendly properties. To exhibit better performance, the structures of these compounds may be modified by changing the reaction conditions and using various surfactants, organic compounds, and additives [28]. In this regard, SBA-15 is a mesoporous material that is prepared by a triblock copolymer surfactant at low pH levels. The synthesized material has thick silica walls and large pore sizes, facilitating the fast mass transfer of ingoing cations. Furthermore, its high thermal stability enables long-term use of the material. However, SBA-15 gradually loses part of its adsorption capacity due to the absence of a binding group on the surface. To eliminate this drawback, modification of the SBA-15 surface by the grafting of organic groups has been suggested [28]. The strong covalent bonds created by the grafting process strongly hold the grafted groups together, leading to long-time application of the sorbent. Obviously, the grafted groups may reduce the pore diameter of the channels, causing a significant decrease in the diffusion rate of cations and hence a slower kinetic sorption rate. Moreover, the bonded organic groups on the surface of the sorbent limit the access of ingoing cations to sorption sites. Therefore, new studies are required to improve the functionalization method for obtaining more satisfactory adsorption performance for the target cation [28].

In the present study, a new sorbent was prepared by functionalizing mesoporous SBA-15 with 1,5-diphenyl carbazide (DPC) to present a new adsorptive system for the efficient removal of Cd from aqueous solutions. The grafted species is chemically stable, highly hydrophilic, and small in size, yielding desirable performance from the studied cation [28, 29]. To achieve optimum efficiency, the adsorption process was studied by the response surface methodology (RSM) technique. The principles of this experimental design approach have been provided in the literature [30, 31, 32, 33, 34].

Table 1.

Experimental factors and levels in the central composite design for adsorption of Cd(II)

Factors UnitSurface factors
LevelStar point
(Low) − 1(Central)(High) + 1−𝛼+𝛼
(A) pH35719
(B) Adsorbent dose mg34517
(C) Initial concentrationmg/L15 25355 45
(D) Contact time min15 202510 30

2. Materials and methods

2.1. Chemical compounds

Pluronic P123 (EO20PO70EO20, Mn = 5800), DPC (C13H14N4O, 97%), hydrochloric acid (HCl, 37%), tetraethylorthosilicate (>99.0%, TEOS), toluene (99.8%), chloropropyltriethoxy silane (CPTES, 97%), ethylene diaminetetraacetic acid (>98.5%), triethylamine (C2H5)3N, >99.5%), and Cd(NO3)2⋅4H2O (98%) were purchased from Sigma-Aldrich.

2.2. Synthesis and functionalization of SBA-15

SBA-15 was synthesized by the hydrothermal method and according to the procedure outlined in [35]. The mixture was prepared by adding 4.00 g of P123 to 85.0 mL of HCl (2.0 M) and then stirring this solution for 2 h at 40 °C. Furthermore, 6.8 mL of TEOS was added, and the mixture was stirred for 18 h, transferred into an autoclave, and finally heated at 100 °C for 22 h. Next, the product was separated, thoroughly rinsed with distilled water, dried at 90 °C, and calcined at 550 °C for 6 h. For functionalization, 50 mL of toluene was added to 1.00 g of the synthesized SBA-15 and stirred for 1 h at 25 °C. After adding 1.0 mL CPTES, the mixture was refluxed for 24 h at 120 °C under N2 atmosphere. Moreover, the chlorinated compound (Cl-SBA-15) was separated and thoroughly rinsed by toluene; it was vacuum-dried at 100 °C. Additionally, 55.0 mL of toluene, 1.2 mL of trimethylamine, and 0.50 g of DPC were then added to 1.0 g Cl-SBA-15. Finally, the mixture was refluxed for 24 h at 115 °C under N2 atmosphere, and the functionalized adsorbent (DPC-SBA-15) was separated and rinsed by toluene and then dried in vacuum at 80 °C [36].

2.3. Adsorption experiments

2.3.1. Statistical and data analysis

The RSM is applied to obtain the optimal response from a limited number of experiments. It is a statistical method for multifactor experiments, and it determines the relationship among various parameters to achieve optimum conditions. In the RSM, the number of experiments (N) is determined by (1) as follows:

N=2K(K1)+C0,(1)
where K is the number of variables and C0 is the center point.

In addition, a quadratic equation (2) is employed to describe the performance of the system.

Y=𝛽0+i=1k𝛽ixi+i=1k𝛽iixi2+1ijk𝛽ijxixj+𝜀,(2)
where Y, 𝛽0, 𝛽i, 𝛽ii, 𝛽ij, and 𝜀 denote the predicted response, the constant coefficient, the linear coefficient, the quadratic coefficient, the interactive coefficient, and the error of the model, respectively [37, 38, 39].

Furthermore, the responses are represented by surface plots showing the interactions between the variables, which determine the optimized conditions of the system. In the present study, the software Design-Expert 7.0.0 is used to evaluate the collective effect of four independent variables (pH, adsorbent dose, initial concentration, and contact time) in sets of 30 experiments. The variables have five levels; the details are presented in Table 1 [40].

2.3.2. Modeling and optimization of adsorption performance

To this end, 40 mL of the Cd2+ solution was added to the adsorbent having a a degree of concentration that was determined by the software (as presented in Table 4) in 30 runs. The table lists the values of pH, adsorbent dose, and contact time for each run of the adsorption process. After performing each run, the sorbent was separated, and the amount of Cd2+ in the solution was measured by atomic absorption spectroscopy (AAS; AAnalyst 300 PerkinElmer, USA; air–acetylene flame at 𝜆 = 228.8 nm). To achieve optimum conditions for the maximum capacity of Cd(II) adsorption (qe) by DPC-SBA-15, all variables (pH, adsorbent dose, initial concentration, and contact time) were set at the determined range. The response (adsorption efficiency) was considered to be maximized in the numerical optimization menu of Design-Expert 7.0.0 [41, 42].

2.3.3. Determination of point of zero charge (pHpzc)

The pH of the surrounding electrolyte determines the surface charge of the adsorbent, which can be calculated by measuring the pHpzc. Five beakers containing 25 mL of NaCl (0.01 M) solution were prepared to determine the pHpzc. This was followed by adding 0.02 g of DPC-SBA-15 to the solution and adjusting the pH to 1, 3, 5, 7, and 9 by adding 0.1 M NaOH or 0.1 M HCl. The solutions were kept under N2 flow for 3 h, and the final pH of each solution was measured accordingly. Then, the pHpzc was obtained by plotting the final versus initial pH values [43, 44, 45, 46].

2.3.4. Adsorption kinetics

The uptake rate of an analyte is a suitable parameter for selecting an adsorbent for application purposes. A series of adsorption experiments was carried out with 40 mL of Cd2+ 25.39 mg/L solutions added to 4.55 mg of the adsorbent at pH 5.75, which was an optimized condition obtained from the software (Table 5), and in a time interval of 0–25 min at 298 K. To investigate the best-fit equation, experimental data were evaluated by the pseudo-first-order and pseudo-second-order kinetic models [47].

2.3.5. Thermodynamics

Some studies have confirmed the effects of temperature on the removal process for obtaining the thermodynamic factors [48, 49]. The corresponding distribution coefficient (Kd) is determined by (3).

Kd=qeCe,(3)
where qe represents the amount of analyte adsorbed onto the adsorbent (mg/g). It can be calculated by (4) as follows:
qe=(C0Ce)×VW,(4)
where C0 and Ce denote the initial and final concentrations (mg/L), respectively, and W and V represent the adsorbent quantity (g) and the volume of the solution (L), respectively. The Gibbs free energy is determined by (5).
𝛥G0=RTlnKd,(5)
where R and T are the universal gas constant (0.0083 kJ∕mol⋅K) and the temperature (K), respectively [50]. To investigate the effect of temperature on Cd adsorption, the sorption process is analyzed at different temperatures from 298.15 to 328.15 K. The temperature is adjusted by using a rotary oven. For this purpose, 40 mL of the Cd2+ 25.39 mg/L solution is added to 4.55 mg of the adsorbent at pH 5.75 for 21.50 min, which was an optimized condition obtained from the software (Table 5). Finally, the thermodynamic parameters of the adsorption process are calculated based on the estimated results.

2.3.6. Adsorption isotherms

The type of adsorption has been determined from the energy of the sorption process in the literature [51, 52]. Isotherms have also been used to describe the distribution of the adsorbate between aqueous solutions and the solid adsorbent surface. Langmuir, Freundlich, and Dubinin–Radushkevich (D–R) models are the isotherms most commonly used for elucidating the nature of adsorption processes. The Langmuir model indicates that monolayer adsorption occurs and that the adsorbed surface is homogeneous [51, 52]. On the other hand, the Freundlich model determines that the phenomenon is multilayer adsorption and that the surface is heterogeneous [47]. The D–R isotherm suggests that ionic adsorbates bind to the most energetically favorable sites. Then, multilayer adsorption can be observed. This isotherm is applied for determining whether the adsorption mechanism is physical or chemical [51, 52].

To analyze sorption isotherms, 40 mL of the Cd2+ 25.39 mg/L solution was added to 4.55 mg of the adsorbent at pH 5.75 for 21.50 min, which was an optimized condition according to the results obtained from the software (Table 5). The parameters required for substitution in Langmuir, Freundlich, and D–R models were estimated, and calculations were performed accordingly.

2.3.7. Adsorbent regeneration and reusability

For this purpose, 40 mL of the Cd2+ 25.39 mg/L solution was added to 4.55 mg of the adsorbent at pH 5.75 for 21.50 min, which was determined as an optimized condition by the software (Table 5). After cation adsorption, the adsorbent was separated and the solid was dried at 60 °C. Finally, regeneration was separately performed using 5 mL HCl and HNO3 at 0.1, 0.2, and 0.3 M concentrations for 120 min. The regenerated adsorbent was reused six times successfully.

2.3.8. Adsorption selectivity

A series of solutions with a Cd2+ concentration of 25.39 mg/L (an optimized condition) and some common competing ions (Na+, Ca2+, Mg2+, Ba2+, Zn2+, Co2+, Mn2+, and Pb2+) in different concentration ranges (5, 10, 15, 20, 40, and 100 mg/L) were prepared in this regard. Then, 40 mL of these solutions was added to 4.55 mg of the adsorbent at pH 5.75 for 21.50 min, which was an optimized condition provided by the software (Table 5). After performing the adsorption process for each competing ion, the sorbent was filtered and the concentration of Cd ions in the solutions was determined by AAS.

3. Results and discussion

3.1. Sample characterization

X-ray diffraction (XRD) is a useful tool for studying the phase purity of solid samples [53, 54]. To this end, small-angle XRD patterns of SBA-15 and DPC-SBA-15 at 0.8–10° 2𝜃 with a rate of 0.05°/s were recorded using an X’PertPro, D8 ADVANCE, Bruker X-ray diffractometer (with a Ni-filtered Cu-K𝛼 radiation source at 1.5406 Å, 40 kV, 30 mA; Netherlands). This is illustrated in Figure 1. The SBA-15 sample displayed three characteristic diffraction lines at 2𝜃 values of 0.83, 1.47, and 1.78°, which originated from (100), (110), and (200) diffraction planes, respectively. Based on the results, no diffraction lines were observed beyond a 2𝜃 value of 2°, indicating that the material was completely amorphous. The pattern was identical to the reference sample corresponding to an ordered two-dimensional hexagonal mesoporous structure [55]. For the DPC-SBA-15 sample, a small shift was observed for the diffraction lines associated with a slight decrease in the d-spacing value, which was related to the grafting of DPC into the SBA-15 structure. Moreover, the intensity of reflection lines decreased in the functionalized sample [56].

Figure 1.

XRD patterns of reference sample SBA-15 [55] (a), synthesized SBA-15 (b), and DPC-SBA-15 (c).

Figure 2.

FTIR spectra of synthesized SBA-15 (a), 1,5-diphenyl carbazide (b), and DPC-SBA-15 (c).

Figure 3.

SEM images of reference sample SBA-15 (Rehman et al. 2017) (a), synthesized SBA-15 (b), and DPC-SBA-15 (c).

Figure 4.

EDAX spectra of synthesized SBA-15 (a), DPC-SBA-15 (b), and Cd-DPC-SBA-15.

In addition, Fourier transform infrared (FTIR) spectra of the synthesized SBA-15 are recorded by an FTIR spectrophotometer (6300 Jasco, Japan) in the range of 350 −−4000 cm−1 (a resolution of 8 cm−1 and a scan number of 6) by using a KBr pellet (Figure 2a). The absorption bands at 802 and 1080 cm−1 are attributed to the symmetric and asymmetric oscillations of Si–O–Si, respectively. Similarly, the bands at 3475 and 3370 cm−1 correspond to the vibration of –OH. Silanol groups are also observed in the DPC-SBA-15 spectrum [57], which is depicted in Figure 2c. In the FTIR spectrum of DPC (Figure 2b), the absorption bands at 931 cm−1 and 1257 cm−1 are attributed to C–C ring breathing and N–H in-plane bending, respectively. The bands at 1448 and 1492 cm−1 are related to C–C vibrations in benzene, and the bands appearing at 1700 and 3085 cm−1 correspond to C =O and =C–H bonds, respectively. In addition, the band at 3335 cm−1 is related to N–H symmetric stretching [58, 59]. In the spectrum of DPC-SBA-15 (Figure 2c), absorption bands attributed to the Si–O–Si and –OH vibrations of silanol groups are observed, indicating that the ligand was grafted into the SBA-15 structure and that the functionalization procedure was performed properly (Figure 2c).

Table 2.

Surface area, pore volume, and pore diameter of SBA-15 and DPC-SBA-15 samples

Adsorbent BET surface area (m2∕g)Pore volume (cm3∕g)Pore diameter (nm)
SBA-15907.651.44 3.22
DPC-SBA-15524.360.82 3.01

BET, Brunauer–Emmett–Teller.

Figure 3 displays the scanning electron microscopy (SEM) images of the reference SBA-15, synthesized SBA-15, and DPC-SBA-15 samples recorded by TESCAN MIRA3 LMU (Czech Republic). The parallel finger-like appearance of the particles of synthesized SBA-15 is approximately identical to that of the reference sample SBA-15. Due to the immobilization of DPC on the surface of SBA-15, the morphology of the DPC-SBA-15 sample becomes smoother and the thread-like structures are fastened to each other [60].

Furthermore, the energy-dispersive X-ray (EDAX) spectra of the synthesized SBA-15, DPC-SBA-15, and DPC-SBA-15 samples loaded with Cd recorded by TESCAN MIRA3 LMU (Czech Republic) are shown in Figure 4. In the spectrum of SBA-15, constituent elements are detected, including O and Si. The presence of carbon and nitrogen is detected in the spectrum of DPC-SBA-15 in addition to peaks related to O and Si, indicating that the ligand was grafted into the SBA-15 structure. Furthermore, the peaks correspond to O, Si, C, and N. The peak related to Cd is observed in the spectrum of DPC-SBA-15 loaded with Cd. Accordingly, the spectra show that the functionalization process was successfully performed and that the functionalized adsorbent adsorbed the target cation (Figure 4).

The thermal curves (thermogravimetric analysis–differential thermogravimetry [TG–DTG]) of the DPC-SBA-15 sample are recorded in nitrogen atmosphere and at 10 °C/min by a NETZSCH STA 409 PC/PG instrument in the range 25–800 °C (Figure 5). The observed weight loss at 25–110 °C is related to the dehydration of H2O molecules adsorbed on the surface of the samples. Moreover, the detected weight loss peak at 160–220 °C is attributed to the decomposition of the ligand [61].

Figure 5.

TG–DTG curves of synthesized DPC-SBA-15.

Figure 6.

Nitrogen adsorption–desorption isotherms of SBA-15 (a) and DPC-SBA-15 (b). The inset shows the BJH pore size distribution.

Table 3.

Analysis of variance for Cd(II) adsorption capacity (Q)

SourceSum of squaresdfMean squareF-valuep-value
Prob > F
Model 49194.88143513.922073.79 <0.0001Significant
(A) pH2301.0412301.041357.99 <0.0001
(B) Adsorbent dose759.381759.38448.16 <0.0001
(C) Initial Cd concentration 27270.041 27270.0416093.80 <0.0001
(D) Time425.041425.04250.84 <0.0001
AB3.0613.061.81 <0.1988
AC10.56110.566.23 <0.0247
AD1.5611.560.92 <0.3521
BC18.06118.0610.66 <0.0052
BD0.06310.0630.037 <0.8503
CD1.5611.560.92 <0.3521
A27308.0017308.004312.92 <0.0001
B22922.8612922.861724.97 <0.0001
C2 12470.861 12470.867359.85 <0.0001
D21421.0711421.07838.67 <0.0001
Residual25.42151.69
Lack of fit18.58101.861.36 <0.3864Not significant
Pure error6.8351.37
Total correction 49220.3029

The N2 adsorption is recorded by PHS1020, and pretreatment is performed under N2 atmosphere at 150 °C in the relative pressure of 88 kPa. The resulting N2 adsorption–desorption isotherms are presented in Figure 6. These isotherms are identical to type IV isotherms, as defined by the International Union of Pure and Applied Chemistry, which is characteristic of mesoporous materials [62]. Based on the obtained data, the inflection position of SBA-15-DPC has slightly shifted to lower pressures, indicating that the pore size decreased after the grafting of DPC on the SBA-15 surface. Additionally, the distributions of the calculated pore from the Barrett–Joyner–Halenda (BJH) plot (inset of Figure 6) show that the diameter of DPC-SBA-15 pores is slightly smaller than that of the SBA-15 pores [63, 64]. Similarly, the specific surface area (524.36 m2∕g) and the pore volume (0.82 cm3∕g) of DPC-SBA-15 are smaller than those of SBA-15 (907.65 m2∕g and 1.44 cm3∕g). However, no significant changes are observed in the pore structure of SBA-15 when it is converted to DPC-SBA-15. This is highly advantageous for ingoing cations with regard to reaching adsorption sites (Table 2).

3.2. Statistical analysis

The analysis of variance (ANOVA) was employed to evaluate the interactions among important variables (Table 3). The data related to the influence of independent variables on the adsorption process were obtained from 30 runs of experiments (Table 4).

Table 4.

Central composite design experiment matrix and experimental results for Cd removal

StdRun pHAdsorbent dose (mg)Initial concentration (mg/g)Time (min)Adsorbent (mg/g)
2215.00 4.00 45.00 20.0061
2325.00 4.00 25.00 10.006
2635.00 4.00 25.00 20.00 159
1849.00 4.00 25.00 20.00 129
257.00 2.50 15.00 15.00 129
963.00 2.50 15.00 25.0089
2175.00 4.005.00 20.0080
3085.00 4.00 25.00 20.00 113
793.00 5.50 35.00 15.00 145
20 105.00 7.00 25.00 20.00 159
12 117.00 5.50 15.00 25.0060
4 127.00 5.50 15.00 15.00 137
5 133.00 2.50 35.00 15.00 150
14 147.00 2.50 35.00 25.00 158
25 155.00 4.00 25.00 20.0075
3 163.00 5.50 15.00 15.00 138
6 177.00 2.50 35.00 15.00 159
8 187.00 5.50 35.00 15.00 157
28 195.00 4.00 25.00 20.00 160
17 201.00 4.00 25.00 20.0077
24 215.00 4.00 25.00 30.00 126
16 227.00 5.50 35.00 25.0053
27 235.00 4.00 25.00 20.00 107
29 245.00 4.00 25.00 20.00 137
10 257.00 2.50 15.00 25.0069
13 263.00 2.50 35.00 25.0061
1 273.00 2.50 15.00 15.006
19 285.00 1.00 25.00 20.00 159
15 293.00 5.50 35.00 25.00 129
11 303.00 5.50 15.00 25.00 129

Table 5.

Optimum conditions derived by RSM design for Cd(II) removal by DPC-SBA-15

Optimum conditionsAdsorption capacity (mg/g)
IonAdsorbent dose (mg) pHIon concentration (mg/L)Contact time (min)QpQe
Cd(II) 4.555.75 25.39 21.50162.832160

In addition, the R2 value is used to study the quality of the polynomial equation, and the statistical significance of the model is evaluated by the F-test. Small p-values (<0.0001) indicate that the model is significant and thus can be used for distinguishing statistically significant parameters. The calculated p-values smaller than 0.05 indicate that the results are predicted at a 5% confidence interval. The lack of fit (LOF) is an important parameter that is related to pure error [65, 66, 67]. In the present study, the LOF value of 1.36 for Cd indicates that the model is suitable for predicting adsorbent performance (Table 3).

The second-order polynomial equation shown in (3) is developed using experimental data, and statistically insignificant coefficients (p-values greater than 0.1) are excluded from calculations [65]. The results (Table 3) reveal that A, B, C, D, AC, BC, A2, B2, C2, and D2 are significant model terms.

Furthermore, the quadratic equation is employed to find the optimum value. The empirical equations between adsorption capacity and input factors in the coded terms are substituted in (6), which is followed by excluding insignificant coefficients (p-values greater than 0.1) according to [68, 69].

QCd=391.19907+44.72917A+38.12037B +13.42083C+12.39167D+0.14583AC +0.040625BC4.08073A24.58796B2 0.21323C20.28792D2.(6)
The predicted R2, which is calculated by the software and is close to 1 (0.9976) and is in good agreement with the adjusted R2 (0.9990), indicates that the response surface quadratic model is quite adequate for predicting the sorption process. Furthermore, the adequate precision value related to the signal-to-noise ratio is higher than 4.0 (166.36), indicating the desirability of the model [65, 70, 71]. Additionally, the coefficient of variance is 1.13, confirming the validity of the data and the model. Finally, the plot of the experimental Q versus the predicted value shows a good fit for the studied cation (Figure 7).

Figure 7.

The plot of actual Q versus predicted Q values for Cd.

3.3. Response surface plots

Graphical plots are used to evaluate the interactions among the studied variables and to obtain the optimum effect of each variable for the maximal adsorption uptake [40]. Figure 8 displays the plots depicting the adsorption of Cd versus pH, adsorbent dose, and the initial concentration.

Figure 8.

Response surface plot for Cd removal. (a) Interaction of pH and initial concentration, (b) interaction of adsorbent dosage and initial concentration.

Figure 9.

(A) Typical curve for the estimation of the pHpzc of DPC-SBA-15. (B) Schematic diagram showing Cd2+ removal by the DPC-SBA-15 adsorbent.

Figure 8a shows the influence of pH and concentration on Cd adsorption in the pH range of 3–7. The sorption capacity of Cd increases up to a pH of 5.75 and then remains nearly constant until a pH of 7. In addition, the measured value of pHpzc indicates that the sorbent surface charge is zero at pH = 4.04 (Figure 9). However, the surface charge is positive at a pH of <4.04, and the uptake of cations is limited because of the repulsion of cations by the positive surface of the adsorbent and the high concentration of H3O+. At pH values higher than the pHpzc, the adsorbent surface charge becomes negative and adsorption gradually increases. Nonetheless, no increase is observed at pH > 6, which is attributed to the partial conversion of Cd2+ to Cd(OH)2 [72]. This is in line with the results obtained by the software (Table 5).

By increasing the initial concentration, the extent of the adsorbed Cd increases and reaches a constant quantity at higher concentrations. This increase is ascribed to the driving force that is created at higher concentrations between adsorption sites and the ingoing cation. Nevertheless, the increase stops at certain concentrations and a steady state is developed, which can be justified by a higher ratio of Cd ions to active sites. The software results (Table 5) perfectly corroborate this conclusion. Finally, the maximal sorption capacity is obtained at 25.39 mg/L of Cd [73].

Figure 8b depicts data on the effect of Cd concentration and sorbent dose. The increase in the uptake of Cd with increasing concentration and sorbent dose is attributed to higher available sorption sites and a higher number of Cd ions. Furthermore, the maximal uptake is observed at 25.39 mg/L of Cd (Table 5). Based on the results, the uptake of Cd increases and then reaches a constant amount with increasing sorbent dose. This increase is ascribed to higher vacant sorption sites although the concentration of the Cd ion is insufficient to engage all adsorption sites with further increase in the amount of the adsorbent. Therefore, the optimized value is obtained with an adsorbent dose of 4.55 mg (Table 5). According to [74], the sorption capacity can be calculated by (4). The typical mechanism for removing Cd2+ cations is shown in Figure 9B.

3.4. Sorption kinetics

The kinetics of the process is studied by a series of experiments performed in the time interval of 0–25 min at 298 K (Figure 10). Equilibrium is attained in 21.50 min, indicating that the process is relatively fast. Then, the data are evaluated by pseudo-first-order and pseudo-second-order kinetic models, respectively, using (7) and (8).

ln(qeqt)=lnqek1t,(7)
tqt=1k2qe2+1qet,(8)
where qe(mgg) and qt (mg∕g) represent sorption capacity values at the equilibrium time and at time t (min), respectively. Moreover, qe is determined by the intercept of the plot ln(qeqt) versus t, and the slope of tqt versus t is considered as the theoretical qe value of the models. In addition, k1 (min−1) and k2 (g/mg/min) are sorption constants. Similarly, the R2 value of 0.9964 indicates that the data are best described by the pseudo-second-order model (Table 6). The calculated q (qe)p value for this model is in agreement with the experimental q (qe)e value [75, 76], the details of which are shown in Table 6 and Figure 10.

Table 6.

Kinetic parameters of pseudo-first-order and pseudo-second-order

Kinetic modelsParametersDPC-SBA-15
Pseudo-first-order(qe)p (mg∕g)140.58
k1 (g/mg/min)0.3262
R20.9583
Pseudo-second-order(qe)p (mg∕g)161.40
k2 (min−1)0.00036
R20.9964

Figure 10.

Effect of contact time and adsorption kinetics on Cd uptake by DPC-SBA-15. The inset shows the linear plot of (5).

3.5. Equilibrium sorption isotherms

The experimental data are analyzed by Langmuir, Freundlich [77], and D–R models. In the Langmuir isotherm, it is assumed that monolayer sorption occurs and the sorbent surface has a finite number of sorption sites with uniform energy [78], which is computed by (9).

Ceqe=1qmb+Ceqm,(9)
where Ce, qe, qm, and b indicate the equilibrium concentration of Cd (mg/L), the equilibrium uptake of Cd (mg/g), the maximal sorption capacity (mg/g), and the Langmuir constant (L/mg), respectively. The plot of (Ceqe) versus (Ce) is presented in Figure 11.

Figure 11.

Langmuir adsorption isotherms for Cd.

The parameter RL is a dimensionless constant and is determined according to (10):

RL=1(1+bC0),(10)
where C0 and b denote Cd concentration (mg/L) and the Langmuir constant (L/mg), respectively. The following definition is given concerning the RL value and the favorability of the process [78]:
 (0<RL<1),unfavorable(RL>1), linear (RL=1),or irreversible (RL=0).

In the Freundlich isotherm, it is assumed that the sorption of cation occurs on the heterogeneous surface and is commonly represented by (11):

logqe=logKf+1nlogCe,(11)
where Kf((mgg)(mgL)1n) and 1∕n are Freundlich constants, respectively, representing sorption capacity and sorption intensity. The sorption is of linear, chemical, and physical type considering that 1∕n = 1, 1∕n < 1, and 1∕n > 1, respectively. According to [78], a 1∕n value close to zero is related to a heterogeneous surface (Figure S1-a).

In the D–R model, it is postulated that first the species binds with the most energetical sites and multilayer sorption takes place accordingly. Furthermore, the model describes the sorption on homogeneous and heterogeneous surfaces in low concentration ranges, and the data of this model are used to determine the physical and chemical adsorption of the process. The D–R model is defined according to (12):

lnqe=lnqmax𝛽𝜀2,(12)
where qe and qmax are predefined parameters. Furthermore, 𝛽 is a coefficient related to average energy (mol2∕kJ2) and 𝜀 denotes a Polanyi potential. The latter is represented by (13) and is depicted in Figure S1-b:
𝜀=RTln1+1Ce.(13)
The free energy change (E in kJ/mol) is the energy required for one mole of species to be transferred on the surface of the sorbent, which can be derived by the D–R model based on (14) as follows:
E=12𝛽.(14)
It is worth noting that E is highly important for estimating the mechanism of sorption and is related to the binding ability. Accordingly, the E values between 8 and 16 kJ/mol demonstrate that the sorption is a chemical process, and E < 8 kJ/mol indicates a physical process [79]. In this study, an E value of 11.38 kJ/mol (in the range of 8–16 kJ/mol) is obtained, indicating that the process is chemisorption [79].

As presented in Table 7, the data corroborate the results of the Langmuir model, showing monolayer sorption on a homogeneous surface with no interaction between Cd ions [78].

Table 7.

Parameters for the Langmuir, Freundlich, and Dubini–Radushkevich isotherms

Isotherm modelsParameters Cd(II)
Langmuirqm (mg∕g)130
RL0.0471
b (L∕mg)0.0063
R20.9902
FreundlichKf (L∕mg)36.4325
R20.9782
n1.739
Dubinin–Radushkevich𝛽 (mol2∕K1⋅J2)0.2504
qm (mg∕g)23
R20.9722
E11.38

Table 8.

Thermodynamic parameters of Cd(II) adsorption by DPC-SBA-15

CationT (K)𝛥G0 (kJ∕mol)𝛥H0 (kJ∕mol)𝛥S0 (kJ∕mol⋅K)R2
Cd(II)29823.57 − 0.036 − 0.0640.9427

Table 9.

Effect of eluents on desorption recovery for metal ions adsorbed on DPC-SBA-15

EluentC (M) Recovery (%) (n = 3)
HNO3 0.1 92 ± 1
0.2 94 ± 1
0.3 94 ± 1
HCl 0.1 84 ± 2
0.2 86 ± 2
0.3 86 ± 2

Table 10.

Effect of potentially interfering ions on Cd(II) removal

Interfering ionCion (mg∕L)q-Error (%)Interfering ionCion (mg∕L)q-Error (%)
Na+0 Zn2+0
5 − 2.245 − 3.02
10 − 4.1110 − 4.57
15 − 8.3015 − 9.60
20 − 12.2520 − 14.02
40 − 19.4840 − 19.25
100 − 28.18100 − 22.71
Co2+0 Mg2+0
5 − 3.255 − 3.68
10 − 4.7010 − 4.41
15 − 7.0315 − 9.27
20 − 10.2520 − 14.45
40 − 16.3740 − 18.90
100 − 22.12100 − 23.41
Mn2+0 Ba2+0
5 − 3.175 − 3.11
10 − 4.1010 − 4.10
15 − 10.7115 − 7.33
20 − 18.0920 − 9.68
40 − 23.4140 − 14.44
100 − 35.53100 − 18.72
Ca2+0 Pb2+0
5 − 3.195 − 4.56
10 − 4.2810 − 6.87
15 − 6.4415 − 12.78
20 − 14.3720 − 19.31
40 − 20.2140 − 26.51
100 − 29.57100 − 37.37

3.6. Thermodynamics of the process

To determine the spontaneity of the process, the calculation of thermodynamic parameters is necessary. Equations (15) and (16) are used in this regard.

lnKd=𝛥H0RT+𝛥S0R(kJmol),(15)
𝛥G0=𝛥H0T𝛥S0(kJmol),(16)
where R, T (K), and Kd denote the gas constant, the temperature, and the equilibrium constant (Kd = qeCe), respectively. The values of thermodynamic parameters are presented in Table 8.

Table 11.

Determination of toxic metals in real samples

Sample Spiked (μg∕L)Found (μg∕L)Recovery (%)
Tap water0Not detected
20 19.41 96.25
River water0Not detected
20 18.90 97.30
Mineral water0Not detected
20 19.37 95.02
Water and0Not detected
wastewater20 19.32 95.26

In addition, negative 𝛥S0 indicates lower randomness of the adsorbed species on the surface of sorbents, arising from strong bonds formed between cations and adsorption sites. Negative 𝛥H0 and positive 𝛥G0 represent the exothermic nature of the process and the nonspontaneous sorption of the cations, respectively. It is reported that the value of thermodynamic parameters is closely related to the type of sorbent, ingoing species, and the type of bonds formed between the adsorbate and the adsorbent surfaces [80, 81, 82, 83].

3.7. Regeneration of the used adsorbent

The study of the regeneration performance of a sorbent determines its potential for repeated applications in wastewater treatment processes. Acidic solutions are typically used for the regeneration of sorbents impregnated with cations. In the present study, Cd is eluted by different acids. The results show that HNO3 is the most effective solution. After adsorption of cations, the adsorbent is separated by filtration; then, the solid is dried at 60 °C and regenerated by the evaluated acids. Next, the regenerated sorbent is used for removing the Cd at optimized conditions (4.55 mg adsorbent dose, a pH of 5.75, an ion concentration of 25.39 mg/L, and a contact time of 21.50 min). Based on the data in Table 9, HNO3 (0.2 M) is the most effective reagent for sorbent regeneration.

After the elution of Cd, the XRD test results reveal that the regenerated sorbent retains its initial form without any significant deterioration. In the first adsorption cycle, the adsorption capacity is 160 mg/g, whereas it decreases to 149 mg/g after six cycles. The related data are displayed in Figure 12 [84].

Figure 12.

Reusability of DPC-SBA-15.

3.8. Selectivity of sorbent

According to their complexation ability, charge density, and hydration degree, the coexisting cations may nearly compete with Cd for adsorption on the surface of DPC-SBA-15. Therefore, this study investigates the potential interfering effect of commonly competing cations. Among the studied cations (Na, Ca, Mg, Ba, Zn, Co, Mn, and Pb), the highest interference effect is exhibited by Pb2+ (Table 10), which can be attributed to the similarity of the radius of its cation to that of Cd. Nonetheless, the interference effect is lower for the remaining cations [85]. To examine the sorbent performance in real samples, the sorbent is used for removing Cd from some real samples. Then, the adsorbent capability is tested on solutions spiked with an intended amount of Cd (Table 11). The results indicate that the recovery is 95%, which is satisfactory [86].

4. Conclusion

Regarding the statistical analysis conducted by Design-Expert 7.0.0 software, Cd adsorption by synthesized DPC-SBA-15 relies on several parameters such as pH, adsorbent dose, initial concentration, and contact time. The results show that a pH of 5.75, an adsorbent dose of 4.55 mg, a Cd concentration of 25.39 mg/L, and an adsorption capacity of 160 mg/g are obtained at optimized conditions. In addition, adsorption by DPC-SBA-15 is a good fit to the pseudo-second-order kinetic model. Furthermore, the experimental data best fit the Langmuir isotherm model, indicating monolayer adsorption on a homogeneous surface. The regenerated sorbent is used for six consecutive cycles, and most of its initial capacity is retained. Finally, the interference of many coexisting cations on Cd removal is negligible in real samples.

Bibliographie


[1] A. Nezamzadeh-Ejhieh; Sh. Hushmandrad Appl. Catal. A, 388 (2010), pp. 149-159 | DOI

[2] A. Nezamzadeh-Ejhieh; N. Moazzeni J. Ind. Eng. Chem., 19 (2013), pp. 1433-1442 | DOI

[3] N. Arabpour; A. Nezamzadeh-Ejhieh Mater. Sci. Semicond. Proces., 31 (2015), pp. 684-692 | DOI

[4] S. Azimi; A. Nezamzadeh-Ejhieh J. Molecul. Catal. A, 408 (2015), pp. 152-160 | DOI

[5] H. Derikvandi; A. Nezamzadeh-Ejhieh J. Hazard. Mater., 321 (2017), pp. 629-638 | DOI

[6] S. Jafari; A. Nezamzadeh-Ejhieh J. Colloid Interf. Sci., 490 (2017), pp. 478-487 | DOI

[7] A. Nezamzadeh-Ejhieh; S. Moeinirad Desalination, 273 (2011), pp. 248-257 | DOI

[8] H. Zabihi-Mobarakeh; A. Nezamzadeh-Ejhieh J. Ind. Eng. Chem., 26 (2015), pp. 315-321 | DOI

[9] A. Niknezhadi; A. Nezamzadeh-Ejhieh J. Colloid Interf. Sci., 501 (2017), pp. 321-329 | DOI

[10] S. Haghshenas; A. Nezamzadeh-Ejhieh New J. Chem., 41 (2017), pp. 13355-13364 | DOI

[11] T. Tamiji; A. Nezamzadeh-Ejhieh J. Electroanal. Chem., 829 (2018), pp. 95-105 | DOI

[12] S. M. A. Abasiyan; F. Dashbolaghi; G. R. Mahdavinia Environ. Sci. Pollut. Res., 26 (2019), pp. 26254-26264 | DOI

[13] T. Tamiji; A. Nezamzadeh-Ejhieh J. Solid State Electrochem., 23 (2019), pp. 143-157 | DOI

[14] T. Tamiji; A. Nezamzadeh-Ejhieh Electrocatalysis, 10 (2019), pp. 466-476 | DOI

[15] M. Nosuhi; A. Nezamzadeh-Ejhieh Electrochim. Acta, 223 (2017), pp. 47-62 | DOI

[16] M. Nosuhi; A. Nezamzadeh-Ejhieh New J. Chem., 41 (2017), pp. 15508-15516 | DOI

[17] J. M. d. Sousa; M. T. Couto; R. J. Cassella Microchem. J., 138 (2018), pp. 92-97 | DOI

[18] A. Nezamzadeh-Ejhieh; M. Shahanshahi J. Ind. Eng. Chem., 19 (2013), pp. 2026-2033 | DOI

[19] K. Vikrant; V. Kumar; K. Vellingiri; K. H. Kim Nano Res., 12 (2019), pp. 1489-1507 | DOI

[20] Q. Zhai; R. Yin; L. Yu; G. Wang; F. Tian; R. Yu; J. Zhao; X. Liu; Y. Q. Chen; H. Zhang; W. Chen Food Control, 54 (2015), pp. 23-30 | DOI

[21] Y. Weng; Z. Weng; Z. Liang; H. Lyu; Z. Zhuang; Y. Yu J. Mater. Chem., 6 (2018), pp. 9528-9538 | DOI

[22] H. Huang; J. Liu; P. Zhang; D. Zhang; F. Gao Chem. Eng. J., 307 (2017), pp. 696-706 | DOI

[23] D. Kasowska; K. Gediga; Z. Spiak Environ. Sci. Pollut. Res., 25 (2018), pp. 824-835 | DOI

[24] G. P. S. Ibrahim; A. M. Isloor; A. M. Asirib; A. F. Ismail; R. Kumar; M. I. Ahamed Chem. Eng. J., 353 (2018), pp. 425-435 | DOI

[25] A. K. Shukla; J. Alam; M. Alhoshan; L. A. Dass; F. A. A. Ali; M. R. Muthumareeswaran; U. Mishra; M. A. Ansari Environ. Sci. Water Res. Technol., 4 (2018), pp. 438-448 | DOI

[26] J. Kheriji; D. Tabassi; B. Hamrouni Water Sci. Technol., 72 (2015), pp. 1206-1216 | DOI

[27] I. Gajda; A. Stinchcombe; J. Greenman; C. Melhuish; I. Ieropoulos Int. J. Hydrog. Energy, 42 (2017), pp. 1813-1819 | DOI

[28] Q. Gao; J. F. Xie; Y. T. Shao; C. Chen; B. Han; K. S. Xia; C. G. Zhou Chem. Eng. J., 313 (2017), pp. 197-206 | DOI

[29] H. R. Pouretedal; S. Basati Iran. J. Catal., 2 (2012), pp. 51-55

[30] S. Ghattavi; A. Nezamzadeh-Ejhieh Int. J. Hydrogen Energy, 45 (2020), pp. 24636-24656 | DOI

[31] M. Nosuhi; A. Nezamzadeh-Ejhieh J. Electroanal. Chem., 810 (2018), pp. 119-128 | DOI

[32] H. Derikvandi; A. Nezamzadeh-Ejhieh J. Colloid Interf. Sci., 490 (2017), pp. 628-641 | DOI

[33] N. Omrani; A. Nezamzadeh-Ejhieh Int. J. Hydrogen Energy, 45 (2020), pp. 19144-19162 | DOI

[34] S. Dharmraj Khairnar; M. Rajendra Patil; V. Shankar Shrivastava Iran. J. Catal., 8 (2018), pp. 143-150

[35] D. Zhao; Q. Huo; J. Feng; B. F. Chmelka; G. D. Stucky J. Am. Chem. Soc., 120 (1998), pp. 6024-6036 | DOI

[36] A. T. Miah; S. K. Bharadwaj; P. Saikia Powder Technol., 315 (2017), pp. 147-156 | DOI

[37] M. Nosuhi; A. Nezamzadeh-Ejhieh Ionics, 24 (2018), pp. 2135-2145 | DOI

[38] H. Derikvandi; A. Nezamzadeh-Ejhieh J. Colloid Interf. Sci., 490 (2017), pp. 652-664 | DOI

[39] Thuan Van Tran; D. Thi Cam Nguyen; H. Thi Ngoc Le; H. Loc Ho; L. Giang Bach C. R. Chim., 22 (2019), pp. 794-803 | DOI

[40] S. Saini; J. Chawla; R. Kumar; I. Kaur SN Appl. Sc., 1 (2019), pp. 894-904 | DOI

[41] M. Nasiri-Ardali; A. Nezamzadeh-Ejhieh Mater. Chem. Phys., 240 (2020), 122142 | DOI

[42] M. S. Shafiof; A. Nezamzadeh-Ejhieh Solid State Sci., 99 (2020), 106071 | DOI

[43] N. Omrani; A. Nezamzadeh-Ejhieh; M. Alizadeh Desal. Water Treat., 162 (2019), pp. 290-302 | DOI

[44] F. Yousefi; A. Nezamzadeh-Ejhieh Desal. Water Treat., 182 (2020), pp. 299-308 | DOI

[45] M. Danesh-Khorasgani; A. Nezamzadeh-Ejhieh J. Solid. State Electrochem., 20 (2016), pp. 2827-2833 | DOI

[46] S. Dianat Iran. J. Catal., 8 (2018), pp. 121-132

[47] M. Borandegi; A. Nezamzadeh-Ejhieh Colloids Surfaces A, 479 (2015), pp. 35-45 | DOI

[48] S. Fakari; A. Nezamzadeh-Ejhieh New J. Chem., 41 (2017), pp. 3811-3820 | DOI

[49] H. Shirzadi; A. Nezamzadeh-Ejhieh J. Mol. Liq., 230 (2017), pp. 221-229 | DOI

[50] M. Heidari-Chaleshtori; A. Nezamzadeh-Ejhieh New J. Chem., 39 (2015), pp. 9396-9406 | DOI

[51] M. Anari-Anaraki; A. Nezamzadeh-Ejhieh J. Colloid Interf. Sci., 440 (2015), pp. 272-281 | DOI

[52] J. Salmani-Mobarakeh; A. Nezamzadeh-Ejhieh Desal. Water Treat., 116 (2018), pp. 158-169 | DOI

[53] A. Nezamzadeh-Ejhieh; S. Tavakoli-Ghinani C. R. Chim., 17 (2014), pp. 49-61 | DOI

[54] M. H. Sheikh-Mohseni; A. Nezamzadeh-Ejhieh Electrochim. Acta, 147 (2014), pp. 572-581 | DOI

[55] T. U. Devi; N. Lawrenceb; R. R. Babuc; K. Ramamurthic; G. Bhagavannarayana J. Miner. Mater. Charact. Eng., 9 (2010), pp. 321-330

[56] M. Chen; H. Zhou; L. Zhou; F. Zhang Polymer, 114 (2017), pp. 180-188 | DOI

[57] D. Macina; A. Opioła; M. Rutkowska; S. Basąg; Z. Piwowarska; M. Michalik; L. Chmielarz Mater. Chem. Phys., 187 (2016), pp. 60-71 | DOI

[58] N. Assi; P. Aberoomand Azar; M. Saber Tehrani; S. W. Husain; M. Darwish; S. Pourmand Technol. Sci. Environ. J. Int., 16 (2018), pp. 4739-4748 | DOI

[59] Y. Zhai; S. Duan; Q. He; X. Yang; Q. Han Microchim. Acta, 169 (2010), pp. 353-360 | DOI

[60] F. Rehman; K. Ahmed; C. Airoldi; S. Gaisford; A. Buanz; A. Rahim; N. Muhammad Mater. Sci. Eng. C, 72 (2017), pp. 34-41 | DOI

[61] Y. W. Fen; A. A. Zainudin; N. E. Safie; W. M. M. Yunus; Z. A. Talib; N. A. Yusof; N. A. S. Omar; W. M. Daniyal; S. Saleviter J. Optoelectron. Adv. Mater., 20 (2018), pp. 537-542

[62] K. S. Sing Pure Appl. Chem., 54 (1982), pp. 2201-2218 | DOI

[63] G. O. Magalhaes; J. O. N. Ribeiro; L. D. C. Vasconcelos; W. L. Vasconcelos Mater. Res., 21 (2018), pp. 148-154 | DOI

[64] J. Zhang; P. Jiang; Y. Shen; W. Zhang; G. Bian J. Porous Mater., 23 (2015), pp. 431-440 | DOI

[65] R. Z. Dorabei; M. S. Darbandsari; A. Moghimi; M. S. Tehrani; S. Nazerdeylami RSC Adv., 6 (2016), pp. 108477-108487 | DOI

[66] H. Derikvandi; A. Nezamzadeh-Ejhieh J. Photochem. Photobiol. A, 348 (2017), pp. 68-78 | DOI

[67] F. Eshraghi; A. Nezamzadeh-Ejhieh Environ. Sci. Pollut. Res., 25 (2018), pp. 14043-14056 | DOI

[68] Y. Li; S. Yang; Q. Jiang; J. Fang; W. Wang; Y. Wang Int. J. Environ. Res., 15 (2018) no. 4, 826 | DOI

[69] S. Senobari; A. Nezamzadeh-Ejhieh Spectrochim. Acta Part A, 196 (2018), pp. 334-343 | DOI

[70] J. Jian Zhang; P. Pingping Jiang; Y. Yirui Shen; W. Weijie Zhang; G. Gang Bian J. Porous Mater., 23 (2015), pp. 440-446

[71] S. Senobari; A. Nezamzadeh-Ejhieh J. Photochem. Photobiol. A, 394 (2020), 112455 | DOI

[72] H. Faghihian; O. Fardmousavi Sop Transactions Appl. Chem., 1 (2014), pp. 29-41 | DOI

[73] S. Mohammadi; H. Faghihian Environ. Sci. Poll. Res., 26 (2019), pp. 12055-12070 | DOI

[74] S. Naeimi; H. Faghihian Sep. Purif. Technol., 175 (2017), pp. 255-265 | DOI

[75] S. Naeimi; H. Faghihian Environ. Toxicol. Pharmacol., 53 (2017), pp. 121-132 | DOI

[76] A. Naghash; A. Nezamzadeh-Ejhieh J. Ind. Eng. Chem., 31 (2015), pp. 185-191 | DOI

[77] Y. Chao; W. Zhu; X. Wu; F. Hou; S. Xun; P. Wu; H. Ji; H. Xu; H. Li Chem. Eng. J., 243 (2014), pp. 60-67 | DOI

[78] Y. Jiang; R. Huang; S. Jiang; Z. Qin; X. Yan Int. J. Phytoremed., 20 (2018), pp. 378-383 | DOI

[79] M. A. Mahmoud J. Basic Appl., 4 (2015), pp. 142-149

[80] Q. Gao; J. F. Xie; Y. T. Shao; C. Chen; B. Han; K. S. Xia; C. G. Zhou Chem. Eng. J., 313 (2016), pp. 197-206 | DOI

[81] N. Esmaeeli; H. Faghihian; S. Naeimi J. Alloys Compd., 744 (2018), pp. 271-280 | DOI

[82] M. Mehrali-Afjani; A. Nezamzadeh-Ejhieh; H. Aghaei Chem. Phys. Lett., 759 (2020), 137873 | DOI

[83] A. Nezamzadeh-Ejhieh; M. Kabiri-Samani J. Hazard. Mater., 260 (2013), pp. 339-349 | DOI

[84] A. M. Sanati; S. Kamari; F. Ghorbani Surf. Interf. Anal., 17 (2019), 100374

[85] S. Naeimi; H. Faghihian Sep. Sci. Technol., 52 (2017), pp. 2899-2908 | DOI

[86] H. Fazelirad; M. A. Taher Measurement, 97 (2017), pp. 23-28 | DOI

Commentaires - Politique


Ces articles pourraient vous intéresser

Equilibrium, isotherms and kinetic studies of uranium sorption onto AlPO 4 -5 and SAPO-5 materials

Naima Bayou; Hamid Aït-Amar; Samir Belkhiri; ...

C. R. Chim (2021)


A novel magnetic biosorbent prepared using an oak shell waste material as an efficient adsorbent for consecutive removal of Pb2+, Ag+, Ba2+, Sr2+, and CrO42− from aqueous solutions

Maryam Adibmehr; Hossein Faghihian

C. R. Chim (2018)


RETRACTED: Application of a novel adsorbent prepared using magnetized Spirulina platensis algae modified by potassium nickel hexacyanoferrate for removal of cesium, studied by response surface methodology

Maryam Azizkhani; Hossein Faghihian

C. R. Chim (2019)