Synthesis and characterization of new pyrochlore solid solution Bi1.5Sb1.5–xNbxCuO7

Mayouf Sellami; Vincent Caignaert; Fatima Z. Kouadri Hanni; Noureddine Bettahar; Naceur Benhadria; Esmahan Sari-Mohammed; Safia Imine; Abdellah Bahmani

doi:10.1016/j.crci.2013.11.005

Synthesis and characterization of new pyrochlore solid solution Bi_1.5Sb_1.5–xNb_xCuO₇

Mayouf Sellami ¹ ; Vincent Caignaert ² ; Fatima Z. Kouadri Hanni ¹ ; Noureddine Bettahar ¹ ; Naceur Benhadria ¹ ; Esmahan Sari-Mohammed ¹ ; Safia Imine ¹ ; Abdellah Bahmani ¹

¹ Laboratoire de chimie des matériaux inorganiques et applications (LCMIA), Faculté de chimie, Université des sciences et de la technologie d’Oran, BP 1505, 31000 El-Mnaouer Oran, Algeria
² Laboratoire de cristallographie et sciences des matériaux, ENSICAEN–CNRS UMR 6508, 6, boulevard du Maréchal-Juin, 14050 Caen cedex 4, France

Comptes Rendus. Chimie, Volume 17 (2014) no. 9, pp. 899-904.

Résumé

New pyrochlore solid solutions Bi_1.5Sb_1.5–xNb_xCuO₇ have been synthesized (0 ≤ x ≤ 1.5) via the ceramic method in the air at 1000 °C. Rietveld refinement of the compounds Bi_1.5Sb_1.5–xNb_xCuO₇ for x = 0, x = 0.75 and x = 1.5 by means of X-ray powder diffraction analysis confirmed an overall A₂B₂O₇ cubic pyrochlore structure according to (Bi³⁺_1.5Cu²⁺_0.5)(Sb⁵⁺_1.5–xNb⁵⁺_xCu²⁺_0.5)O₇ formula with 10.42009 (3) Å, 10.47193 (3) Å and 10.52679(4) Å, respectively, and $F d \bar{3} m$ space group. Composition dependencies of cell parameters show a linear increase with the niobium x fraction. The magnetic susceptibility measurements achieved between 4 and 400 K indicate a paramagnetic behavior with an oxidation state “+2” for the copper ion. The electric resistivity measured using complex impedance spectroscopy evidences an increase of the electric conductivity with temperature and niobium substitution.

Métadonnées

Reçu le : 2013-07-29
Accepté le : 2013-11-05
Publié le : 2014-07-11

DOI : 10.1016/j.crci.2013.11.005

Mots clés : Pyrochlore, Oxides, Synthesis, Solid solutions

Affiliations des auteurs :

Mayouf Sellami ¹ ; Vincent Caignaert ² ; Fatima Z. Kouadri Hanni ¹ ; Noureddine Bettahar ¹ ; Naceur Benhadria ¹ ; Esmahan Sari-Mohammed ¹ ; Safia Imine ¹ ; Abdellah Bahmani ¹

@article{CRCHIM_2014__17_9_899_0,
     author = {Mayouf Sellami and Vincent Caignaert and Fatima Z. Kouadri Hanni and Noureddine Bettahar and Naceur Benhadria and Esmahan Sari-Mohammed and Safia Imine and Abdellah Bahmani},
     title = {Synthesis and characterization of new pyrochlore solid solution {Bi\protect\textsubscript{1.5}Sb\protect\textsubscript{1.5{\textendash}\protect\emph{x}}Nb\protect\textsubscript{\protect\emph{x}}CuO\protect\textsubscript{7}}},
     journal = {Comptes Rendus. Chimie},
     pages = {899--904},
     publisher = {Elsevier},
     volume = {17},
     number = {9},
     year = {2014},
     doi = {10.1016/j.crci.2013.11.005},
     language = {en},
}

TY  - JOUR
AU  - Mayouf Sellami
AU  - Vincent Caignaert
AU  - Fatima Z. Kouadri Hanni
AU  - Noureddine Bettahar
AU  - Naceur Benhadria
AU  - Esmahan Sari-Mohammed
AU  - Safia Imine
AU  - Abdellah Bahmani
TI  - Synthesis and characterization of new pyrochlore solid solution Bi1.5Sb1.5–xNbxCuO7
JO  - Comptes Rendus. Chimie
PY  - 2014
SP  - 899
EP  - 904
VL  - 17
IS  - 9
PB  - Elsevier
DO  - 10.1016/j.crci.2013.11.005
LA  - en
ID  - CRCHIM_2014__17_9_899_0
ER  -

%0 Journal Article
%A Mayouf Sellami
%A Vincent Caignaert
%A Fatima Z. Kouadri Hanni
%A Noureddine Bettahar
%A Naceur Benhadria
%A Esmahan Sari-Mohammed
%A Safia Imine
%A Abdellah Bahmani
%T Synthesis and characterization of new pyrochlore solid solution Bi1.5Sb1.5–xNbxCuO7
%J Comptes Rendus. Chimie
%D 2014
%P 899-904
%V 17
%N 9
%I Elsevier
%R 10.1016/j.crci.2013.11.005
%G en
%F CRCHIM_2014__17_9_899_0

Mayouf Sellami; Vincent Caignaert; Fatima Z. Kouadri Hanni; Noureddine Bettahar; Naceur Benhadria; Esmahan Sari-Mohammed; Safia Imine; Abdellah Bahmani. Synthesis and characterization of new pyrochlore solid solution Bi_1.5Sb_1.5–xNb_xCuO₇. Comptes Rendus. Chimie, Volume 17 (2014) no. 9, pp. 899-904. doi : 10.1016/j.crci.2013.11.005. https://comptes-rendus.academie-sciences.fr/chimie/articles/10.1016/j.crci.2013.11.005/

Version originale du texte intégral

1 Introduction

Pyrochlore-type oxides have attracted great attention for a long time due to their remarkable physical and chemical properties as high thermal stability, high resistance to radiation damage and low thermal conductivity. These properties entitle them to extensive applications, for instance as catalysts [1,2], ionic/electric conductors [3], lithium ion batteries [4], radiation-damage-resistant materials [5], nuclear waste disposal [6,7], thermal barrier coatings [8] or solid electrolytes in high temperature fuel cells [9]. Pyrochlore oxides have the general formula A₂B₂O₆O′ with z = 8; A, B are cations and O, O′ are anions. Most pyrochlore oxides crystallize in space group $F d \bar{3} m$ (#227). Of the four possible choices of origin in this space group, the most commonly used places are the smaller B-type cation at the 16c site with the larger A-type cation at 16d. There are two anion sites, with O at 48f, and O′ at 8b. There are only two variable structural parameters, the cubic lattice parameter a, and the positional parameter x, for the O atom in 48f. The pyrochlore structure can be described as interpenetrating BO₆ octahedra and A₂O′ chains [10,11]. The B₂O₆ framework consists of [BO₆] octahedra sharing all vertices to form large cavities [12]. From extensive experimental work on the synthesis and structural characterization of cubic pyrochlores, stability fields have been proposed for allowable substitution into the A and B cation sites based on measures, such as the ratio of the cation radii size and the cation electronegativity [13]. These new pyrochlore solid solutions Bi_1.5Sb_1.5–xNb_xCuO₇ will be used in the future as catalysts [14]. Here, we report the synthesis and the study of the corresponding structural, magnetic and electric properties.

2 Experimental

The solid solutions were prepared by solid-state reaction of stoichiometric amounts of reagent-grade Bi₂O₃ (99.9%), Sb₂O₃ (99%), Nb₂O₅ (99%) and CuO (99%) (Aldrich Chemical Company Ltd). The mixtures were ground for 1 h with an agate mortar and pestle. The resulting powders were calcined at 500 °C for 24 h in an alumina crucible. Then, the powders were again ground and calcined two more times successively at 700 °C and 900 °C for 48 h each. The resulting powders were re-milled for 1/2 h and uniaxially pressed into pellets about 13 mm in diameter and 2 mm in thickness. Then, they were sintered at 1000 °C for 48 h in the air. The samples’ color was brown. The specimens were initially characterized by X-ray powder diffraction using a PANalytical X’Pert Pro X-ray diffraction system. Data were collected using Cu Kα radiation. Rietveld refinement [15] of the X-ray powder diffraction data was carried out using the FULLPROF program [16]. Polished specimens were examined using a conventional Philips SEM XL30 scanning electron microscope. The magnetic susceptibility of powder samples was measured from 4 to 400 K with SQUID. Electrical conductivity measurements were carried out using an impedance lock-in EG&G 7220-type with a 10-mV AC signal amplitude at frequencies between 30 Hz and 120 kHz.

3 Results and discussion

3.1 Structural characterization

3.1.1 Study of Bi_1.5Sb_1.5–xNb_xCuO₇ solid solution

Previous studies [17] showed that the substitution of copper by manganese in compound Bi_1.5Sb_1.5CuO₇ [18] forms a continuous solid solution with a pyrochlore structure. Here, we substitute antimony by niobium according to this system: Bi_1.5Sb_1.5–xNb_xCuO₇. Fig. 1 shows X-ray diffraction patterns of as-synthesized Bi_1.5Sb_1.5–xNb_xCuO₇. All the diffraction lines in each pattern can be well indexed in the pyrochlore pattern (ICSD 01-077-8429). The results indicated that all compounds had a single cubic pyrochlore structure of Bi_1.5Sb_1.5–xNb_xCuO₇ belonging to space group $F d \bar{3} m$ (No. 227). Using Scherrer's equation [19], the crystallite sizes of the samples were calculated from the size effect contribution to the peak half-width of the (2 2 2) peak and were found to be in the 100–140 nm range. These size limits depend on the ceramic preparation method (high temperature). It was worth noting that the diffraction peaks of the samples were shifted toward a smaller diffraction angle as a result of the increasing Nb doping content, indicating that the lattice parameters had increased according to Vegard's law [20] Effectively, the cell parameters were practically on the correlation line, indicating that the difference between the niobium ionic radius, R_Nb(VI) = 0.72 Å, and the antimony ionic radius, R_Sb(VI) = 0.60 Å [21], is the reason of this increase in the lattice constant. Fig. 2 shows SEM photographs of the surface morphologies of the disk samples. It was found that the grain size of the samples slightly changes with increasing x. Samples with x = 0 and 0.5 seem to be rounded, whereas sharp grain edges are evidenced for x = 1. The difference in the grain growth rate during sintering, which causes the variation in grain size, is attributed to the different diffusion rates of the ionic species.

Fig. 1
(Color online.) XRD patterns of Bi_1.5Sb_1.5–xNb_xCuO₇ solid solutions.

Fig. 2
SEM micrograph of Bi_1.5Sb_1.5–xNb_xCuO₇ compounds (x = 0; x = 0.5; x = 1; x = 1.5).

3.1.2 Structural refinement

The highly symmetrical ideal pyrochlore structure A₂B₂O₇ crystallizes in space group $F d \bar{3} m$ with A and B cations on two special positions (16d, 16c) and oxygen atoms on two sites, 48f O and 8b O′, resulting in a single positional variable (x for the 48f site oxygen atoms in the B₂O₆ octahedral network). Rietveld refinement with this model shows that copper is statistically distributed on the A and B sites, leading to formula (Bi_1.5Cu_0.5)(Sb_1.5–xNb_xCu_0.5)O₇. As expected, this model results in anomalously large thermal parameters for the A site cations and the O′ oxygen atoms in this initial refinement. The disordered structure was therefore modelled assuming static displacements of the A and O′ atoms, similar to that of analogous Bi–M–Nb–O pyrochlores (M = Zn [22], Fe [23], Mn [24]), whose structures were refined using neutron powder diffraction data. The refinement of the positional parameters for the disordered metal sites was carried out assuming displacements of the A₂O′ network, as found for a number of other pyrochlore compounds [25–28]. Refinement without displacement of the A site Bi/Cu gave bad residuals for the smallest reflections. Improved results were obtained with Bi/Cu displaced to six partially filled 96g sites and O′ site displaced to the 32e site. Observed, calculated and difference X-ray powder diffraction spectra are displayed in Fig. 3. The agreement between the observed and calculated profile is excellent and R_Bragg factors ≤ 6.54; they depend on both the atomic coordinates and the chemical composition. The final refinement results are given in Tables 1 and 2. The pyrochlore structure, (Bi_1.5Cu_0.5)(Sb_1.5–xNb_xCu_0.5)O₇, can be described by the interpenetrating networks of (Sb_1.5–xNb_xCu_0.5)O octahedra and intersecting (Bi_1.5Cu_0.5)O′ chains, where A cations are in the 96g position and O′ anions are in the 32e position. Fig. 4 illustrates the displacive disorder of the A₂O′ network. The arrangement of the octahedra, sharing vertices, generates hexagonal cavities where the A sites are located. The little red spheres represent the oxygen atoms and the yellow spheres are niobium/copper atoms. The blue spheres represent the six equivalent 96g sites for the A site Bi/Cu cations, and the large red spheres denote the 4 possible displaced positions for the O′ oxygens. (For interpretation of the references to color in Fig. 4, the reader is referred to the web version of this article).

Fig. 3
(Color online.) Observed, calculated and difference X-ray powder diffraction patterns of Bi_1.5Nb_1.5CuO₇.

Sample	x = 0	x = 0.75	x = 1.5
Global formula	Bi₁₂Cu₈Sb₁₂O₅₆	Bi₁₂Cu₈Sb₆Nb₆O₅₆	Bi₁₂Cu₈Nb₁₂O₅₆
Formula mass	5373.6 g	5200.2 g	5026.88 g
Crystalline system	Cubic	Cubic	Cubic
Space group	$F d \bar{3} m$	$F d \bar{3} m$	$F d \bar{3} m$
Cell parameter	10.42009(3) Å	10.47193(3) Å	10.52679(4) Å
Cell volume	1131.393(6) Å³	1148.366(6) Å³	1166.510(8) Å³
Wyckoff sequence	fdcb	fdcb	fdcb
Number of reflexion	74	74	73
Number of refined parameters	14	17	14
Function profile	Pseudo-Voigt	Pseudo-Voigt	Pseudo-Voigt
R_wp	3.67	3.35	2.97
R_p	2.59	2.41	2.36
R_exp	2.03	1.86	2.32
R_Bragg	6.51	5.72	6.54

	Atom	Position	Site occupancy	x	y	z	B_iso [Å²]
x = 0	Bi(1)/Cu(1)	96g	0.125/0.041	0.5076(7)	0.5076(7)	0.4709(9)	0.10(9)
	Sb(2)/Cu(2)	16c	0.75/0.25	0	0	0	0.10(5)
	O1	48f	1	0.3243(9)	1/8	1/8	1.7(3)
	O2	32e	1/4	0.346(3)	0.346(3)	0.346(3)	1.7(3)
x = 0.75	Bi(1)/Cu(1)	96g	0.125/0.041	0.5101(7)	0.5101(7)	0.4705(9)	0.10(9)
	Sb(2)/Nb(2)/Cu(2)	16c	0.375/0.375/0.25	0	0	0	0.60(9)
	O1	48f	1	0.3239(8)	1/8	1/8	1.4(3)
	O2	32e	1/4	0.342(1)	0.342(1)	0.342(1)	1.4(3)
x = 1.5	Bi(1)/Cu(1)	96g	0.125/0.041	0.5140(9)	0.5140(9)	0.4697(9)	0.90(9)
	Nb(2)/Cu(2)	16c	0.75/0.25	0	0	0	0.10(4)
	O1	48f	1	0.3154(6)	1/8	1/8	1.4(3)
	O2	32e	1/4	0.354(3)	0.354(3)	0.354(3)	1.4(3)

Fig. 4
(Color online.) (Bi_1.5Cu_0.5)(Nb_1.5Cu_0.5)O₇ cubic pyrochlore structure.

3.2 Magnetic susceptibility

Magnetic data obtained for the compounds indicate that the samples were overall paramagnetic in nature, with an effective moment of 1.74(5) and 1.70(3) μ_B for the copper in compounds Bi_1.5Sb_1.5CuO₇ and Bi_1.5Nb_1.5CuO₇. The inverse susceptibility versus temperature data for the Bi_1.5Nb_1.5CuO₇ show upward curvature at the lowest temperatures and at high temperatures deviate somewhat from a linear Curie–Weiss behavior (regions between 200 and 300 K). The observed effective magnetic moments (μ_eff/mol Cu), calculated from the slopes of the Curie–Weiss fits indicates the “2 + ” oxidation state of the copper. The temperature dependence of the magnetic susceptibility and its inverse are shown in Fig. 5. The copper oxidation state confirm the pyrochlore formula (1.5–1.5–1-7 compound), since bismuth has a “3 + ” and niobium and antimony [29] have a “5 + ” oxidation state.

Fig. 5
(Color online.) Susceptibility and inverse susceptibility versus temperature of Bi_1.5Sb_1.5CuO₇ and Bi_1.5Nb_1.5CuO₇.

3.3 Electrical characterization

Fig. 6 shows the temperature dependence of the total conductivity of Bi_1.5Sb_1.5–xNb_xCuO₇ ceramics, obtained from AC electrical measurements and impedance plots over the temperature range between 300 and 800 K in the air. Clearly, the total conductivity of Bi_1.5Sb_1.5–xNb_xCuO₇ ceramics gradually increases with increasing temperature from 300 to 800 K. The temperature dependence of the total conductivity of Bi_1.5Sb_1.5–xNb_xCuO₇ ceramics can be described by the Arrhenius equation, σ T = σ₀ exp (–E/k_B T) where σ, T, σ₀, E, and k_B are the total conductivity, absolute temperature, pre-exponential factor, activation energy and Boltzmann constant, respectively. The total conductivity data follow a linear behavior, which confirms that the electrical conductivity process is thermally activated. The activation energy for the total conductivity of Bi_1.5Sb_1.5–xNb_xCuO₇ ceramics slightly decrease with increasing the niobium content. The activation energies were determined as 0.45, 0.42 and 0.41 eV for the samples doped with x = 0, 0.5 and 1, respectively. The decrease in the activation energy is the result of an increasing in the conductivity with increasing the Nb content, and reflects the impurity level shift toward the conduction or valence band by increasing the number of sharing electrons or holes. All compounds are considered as semi-conductors.

Fig. 6
(Color online.) Conductivity variation versus inverse temperature (1/T) of Bi_1.5Sb_1.5–xNb_xCuO₇ compound.

4 Conclusion

A new pyrochlore solid solution with formula Bi_1.5Sb_1.5–xNb_xCuO₇ was synthesized by solid-state reaction at 1000 °C. All samples had a single cubic pyrochlore structure of Bi_1.5Sb_1.5–xNb_xCuO₇ with space group $F d \bar{3} m$ (No. 227). The lattice constant increased linearly with increasing niobium concentration. Rietveld refinements confirmed an overall B₂O₆·A₂O′ cubic pyrochlore structure with Cu cations on both A and B sites. Magnetic characterization measurements confirmed a “+2” oxidation state of the copper cation. Electric measurements at high temperature revealed an increase in the electrical conductivity, with a decrease in the activation energy. Our synthesized compounds are considered as semi-conductors.

Acknowledgment

This work was supported by PNR 2011 (Projet national de recherche) of MESRS-Algeria with the collaboration of CRISMAT Laboratory.

Bibliographie

[1] J.M. Sohn; M.R. Kim; S.I. Woo Catal. Today, 83 (2003), p. 289

[2] K. Li; H. Wang; H. Yan J. Mol. Catal. A: Chem., 249 (2006), p. 65

[3] T. Yu; H.L. Tuller Solid State Ionics, 177 (1996), p. 86

[4] N. Sharma; G.V. Rao Subba; B.V.R. Chowdari J. Power Sources, 159 (2006), p. 340

[5] K.E. Sickafus; L. Minervini; R.W. Grimes; J.A. Valdez; M. Ishimaru; F. Li; K.J. McClellan; T. Hartmann Science, 289 (2000), p. 748

[6] J. Lian; S.V. Yudintsev; S.V. Stefanovsky; L.M. Wang; R.C. Ewing J. Alloys Compd., 444–445 (2007), p. 429

[7] S. Lutique; D. Staicu; R.J.M. Konings; V.V. Rondinella; J. Somers; T. Wiss J. Nucl. Mater., 319 (2003), p. 59

[8] X.Q. Cao J. Mater. Sci. Technol., 23 (2007), p. 15

[9] J. Garcia-Barriocanal; A. Rivera-Calzada; M. Varela; Z. Sefrioui; M.R. Díaz-Guillén; K.J. Moreno; J.A. Díaz-Guillén; E. Iborra; A.F. Fuentes; S.J. Pennycook; C. Leon; J. Santamaría Chem. Phys. Chem., 10 (2009), p. 1003

[10] M.A. Subramanian; G. Aravamudan; G.V.S. Rao Prog. Solid State Chem., 15 (1983), p. 55

[11] B.C. Chakoumakos J. Solid State Chem., 53 (1984), p. 120

[12] H. Von Gaertner Neues Jahrb. Miner. Geol. Palaeontol., 61 (1931), p. 1

[13] J.C. Nino Materials Science and Engineering, The Pennsylvania State University, University Park, PA, 2002

[14] M. Sellami; F. Merabat; N. Bettahar; A. Bahmani; S. Imine; E. Sari-mohamed; N. Benhadria Synthèse et caractérisation d’une nouvelle solution solide de type pyrochlore de formule Bi_1,56Sb_1,48Co_0,96–xFe_xO₇, Université Mentouri, Constantine, Algeria, 12–13 December (2012)

[15] M.A. Subramanian; B.H. Toby; A.P. Ramirez; W.J. Marshall; A.W. Sleight; G.H. Kwei Science, 273 (1996), p. 81

[16] C.A. Mims; A.J. Jacobson; R.B. Hall; J.T. Lewandowski J. Catal., 153 (1995) no. 2, p. 197

[17] M. Sellami; V. Caignaert; M. Hamdad; A. Bekka; N. Bettahar J. Alloys Compd., 482 (2009), p. 13

[18] M. Sellami; A. Bekka; N. Bettahar C. R. Chimie, 8 (2005), p. 1129

[19] A.L. Patterson The Scherrer formula for X-ray particle size determination, Phys. Rev., Volume 56 (1939), p. 978

[20] A.R. West Solid State Chemistry and its Applications, Wiley, New Delhi, 1984

[21] R.D. Shannon Acta Crystallogr., A32 (1976), p. 751

[22] I. Levin; T.G. Amos; J.C. Nino; T.A. Vanderah; C.A. Randall; M.T. Lanagan J. Solid State Chem., 168 (2002), p. 69

[23] M.W. Lufaso; T.A. Vanderah; I.M. Pazos; I. Levin; J.C. Nino; V. Provenzano; P.K. Schenck J. Solid State Chem., 179 (2006), p. 3900

[24] T.A. Vanderah; M.W. Lufaso; A.U. Adler; I. Levin; J.C. Nino; V. Provenzano; P.K. Schenck J. Solid State Chem., 179 (2006), p. 3467

[25] M. Ganne; K. Toyama Mater. Res. Bull., 10 (1975), p. 1313

[26] M. Avdeev; M.K. Haas; J.D. Jorgensen; R.J. Cava J. Solid State Chem., 24 (2002), p. 169

[27] L.Q. Li; B.J. Kennedy Chem. Mater., 15 (2003), p. 4060

[28] U. Ismunandar; T. Kamiyama; K. Oikawa; A. Hoshikawa; B.J. Kennedy; Y. Kubota; K. Kato Mater. Res. Bull., 39 (2004), p. 553

[29] M. Sellami; N. Ngyen; A. Bekka; N. Bettahar C. R. Chimie, 9 (2006), p. 1209

Commentaires - Politique

Ces articles pourraient vous intéresser

Synthesis and characterization of the new pyrochlore Bi_1.5Sb_1.5−xNb_xMnO₇ solid solution

Mayouf Sellami; Vincent Caignaert; Merième Hamdad; ...

C. R. Chim (2011)

Crystallographic, magnetic and electric studies of a new pyrochlore-like structure (Bi_1.56Co_0.44)(Sb_1.48Co_0.52)O₇ compound

Mayouf Sellami; Ahmed Bekka; Noureddine Bettahar; ...

C. R. Chim (2009)

Safe management of actinides in the nuclear fuel cycle: Role of mineralogy

Rodney C. Ewing

C. R. Géos (2011)